Formation of Copper Nanoparticles in LTL Nanosized Zeolite: Kinetics Study

by Anastasia KharchenkoOleg I LebedevVladimir ZholobenkoVincent De Waele, and Svetlana Mintova
J. Phys. Chem. C, Just Accepted Manuscript


The kinetics of formation of copper nanoparticles in LTL type nanosized zeolite (Cu0 -LTL) was investigated. The water suspensions containing copper ion exchanged zeolite crystals (Cu2+-LTL) were treated with three reducing agents (hydrazine monohydrate, triethylamine and sodium borohydride) under identical conditions. With triethylamine, copper particles (Cu0 NPs) were not formed, while with sodium borohydride, a rapid reduction of Cu2+ leading to Cu0 nanoparticles predominantly located on the external surface of the LTL zeolite nanocrystals was observed. Whereas the reaction with hydrazine led to slow reduction and formation of Cu0 NPs within the LTL zeolite channels. The kinetics of formation of Cu0 NPs in the LTL zeolite suspension was investigated by in situ UV-Vis spectroscopy. Additionally, the solid samples (pure LTL, Cu2+-LTL and Cu0-LTL) were isolated before and at different stages of reduction, and investigated with XRD, nitrogen sorption and high-resolution transmission electron microscopy (HRTEM). The initial copper nanoparticles with a size of 0.2 – 1.6 nm were observed after 190 min of reduction in the presence of hydrazine, and under prolonged treatment (from 280 min to 960 min), the copper nanoparticles tend to migrate to the external surface of the zeolite crystals and aggregate into large copper entities. The structure of the nanosized LTL zeolite crystals was preserved from the initial to the final stages of reduction.


We acknowledge the financial support provided by TAR-G-ED ANR project.

Source : Formation of Copper Nanoparticles in LTL Nanosized Zeolite: Kinetics Study – The Journal of Physical Chemistry C (ACS Publications)

Scroll to Top